Influence of annealing temperature on the properties of ZnO:Zr films deposited by direct current magnetron sputtering

Transparent conducting zirconium-doped zinc oxide (ZnO:Zr) films were deposited on quartz substrates by direct current (DC) magnetron sputtering at room temperature. The influence of post-annealing temperature on the structural, morphological, electrical and optical properties of ZnO:Zr films were investigated. When annealing temperature increases from room temperature to 573 K, the resistivity decreases obviously due to an improvement of the crystallinity. However, with further increase in annealing temperature, the crystallinity deteriorates leading to an increase in resistivity. The films annealed at the optimum annealing temperature of 573 K in vacuum have the lowest resistivity of 9.8 × 10−4 Ω cm and a high transmittance of above 92% in the visible range.