Surface treatment and corrosion behaviour of Fe–32Mn–6Si shape memory alloy

Fe–Mn–Si-based shape memory alloys are characterized by a good shape-memory effect, but with a modest corrosion resistance. The goal of this study is to try out a suitable surface treatment in order to improve the corrosion resistance of the Fe–32Mn–6Si alloy without impairing its shape-memory properties. The implemented solution is a zinc-electrodeposited coating achieved by chromium conversion treatment. The results show, thanks to electrochemical and thermomechanical measurements, and corrosion tests performed in salt spray chamber, that zinc-electrodeposited coating followed by chromium conversion layer can be considered as a good anticorrosion solution of the Fe–32Mn–6Si alloy.

RésuméLes alliages à mémoire de forme de type Fe–Mn–Si sont caractérisés par un bon effet mémoire de forme, mais par une faible résistance à la corrosion. Le but de cette étude est d'envisager un traitement de surface approprié permettant d'améliorer la résistance à la corrosion de l'alliage Fe–32Mn–6Si sans altérer sa propriété de mémoire de forme. La solution mise au point est un revêtement électrolytique de zinc, suivi d'un traitement de chromatation. Les résultats montrent, grâce aux mesures électrochimiques et thermomécaniques et aux essais de corrosion réalisés dans une chambre de brouillard salin, que le revêtement de zinc électrolytique suivi d'un traitement de chromatation peut être considéré comme une bonne solution anticorrosion de l'alliage Fe–32Mn–6Si.