FeCo nanowire arrays have been obtained by current pulse electrodeposition into nanoporous alumina templates. First-order reversal curve (FORC) diagrams have been used to investigate magnetostatic interaction and average coercivity of individual FeCo nanowires embedded in porous alumina templates. The FeCo nanowires with a wires length up to 3 μm and wires diameter ranging from 25 to 50 nm showed interacting single-domain behavior. Using FORC diagrams, the spread of coercivity distribution was seen to be almost independent of the wires diameter, but with increase in diameter the inter-wire magnetostatic interaction was increased. It was found that for arrays with higher diameter, the coercivity of the arrays is lower than the average coercivity of the individual wires. It was detected that an increase in wire diameter results in a considerable increase in the spread of the distribution in the Hu direction of FORC distribution. Curve fitting on the experimental data proved a relatively linear relation between interaction field and square diameter of the nanowires.
► Fabrication of CoFe nanowires through ac electrodeposition.
► Magnetostatic interaction between nanowires through FORC investigation.
► Enhancing the pore diameter leads to a reduced Hc and squareness.
Journal: Current Applied Physics - Volume 13, Issue 4, June 2013, Pages 664–669