• MOF-53(Fe)/RGO composite was fabricated by a one-step hydrothermal strategy.
• The morphology, microstructure, magnetic and electromagnetic properties were investigated.
• The maximum reflection loss of MOF-53(Fe)/RGO composite can reach −25.8 dB at 15.4 GHz with the thickness of 2 mm.
• The absorption bandwidths exceeding −10 dB are 12.2 GHz (from 5.8 to 18 GHz) in the range of 1.5–4 mm.
A novel metal organic framework (MOF) coated RGO was fabricated by a one-step method. The morphology and microstructure of MOF-53(Fe)/RGO composite were characterized by XRD and TEM. The electromagnetic parameters indicate that MOF-53(Fe)/RGO composite shows enhanced electromagnetic absorption properties compared with MOF-53(Fe). The maximum RL can reach −25.8 dB at 15.4 GHz and the absorption bandwidth with the reflection loss exceeding −10 dB is 5.9 GHz (from 12.1 to 18 GHz) with the thickness of 2 mm. The possible absorption mechanism was also investigated in detail. Our results indicate the potential application of MOF/RGO composite as a more efficient microwave absorber.
Figure optionsDownload as PowerPoint slide
Journal: Journal of Magnetism and Magnetic Materials - Volume 416, 15 October 2016, Pages 226–230