Effect of multielement doping on low-field magnetotransport in La0.7âxMmxCa0.3MnO3 (0.0⩽x⩽0.45) manganite
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
فیزیک و نجوم
فیزیک ماده چگال
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Effect of multielement doping on low-field magnetotransport in La0.7âxMmxCa0.3MnO3 (0.0⩽x⩽0.45) manganite Effect of multielement doping on low-field magnetotransport in La0.7âxMmxCa0.3MnO3 (0.0⩽x⩽0.45) manganite](/preview/png/1802220.png)
چکیده انگلیسی
We report the synthesis, structure and low-field magnetotransport properties of Mischmetal (Mm)-doped La0.7âxMmxCa0.3MnO3 (0⩽x⩽0.45) manganite. Mischmetal-Mm-is a natural mixture of rare earth elements La, Ce, Pr and Nd with â¼28%, 50%, 6% and 16% composition, respectively. All the samples crystallize in orthorhombic structure. Increasing x (Mm), corresponding to decreasing the La-site average ionic radii (ãrAã) hence increasing the size mismatch (i.e. variance Ï2), results in strong suppression of ferromagnetism (TC) and the associated metallicity (TIM). It may be pointed out that Mm (La, Ce, Pr and Nd) substitution has been done to create two effects. First, creation of multivalence of Mn (2+, 3+ and 4+) via Ce substitution and second to create higher degree of disorder due to size difference brought in not only by Ce but also by Pr and Nd. Evidences and arguments based on XPS analysis suggest that multivalent ions La, Mm and Ca, and the resulting presence of Mn2+, Mn3+ and Mn4+, causes the simultaneous operation of ferromagnetism-double exchange (Mn2+/Mn3+ and Mn3+/Mn4+) and antiferromagnetic-superexchange (Mn3+/Mn3+ and Mn2+/Mn2+) interaction. In addition, Mm doping also creates inhomogenities at La-as well as Mn-site due to size and valency difference. A curiously huge magnetoresistance as high as â¼63% for x=0.35, under a moderate magnetic field of â¼10 kOe has been observed and even at low magnetic field of â¼3 kOe MR is â¼30%. The competing double exchange and superexchange coupled with inhomogenities are the most likely cause for the occurrence of large â¼63% CMR in the Mm-doped LCMO.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Magnetism and Magnetic Materials - Volume 321, Issue 12, June 2009, Pages 1814-1820
Journal: Journal of Magnetism and Magnetic Materials - Volume 321, Issue 12, June 2009, Pages 1814-1820
نویسندگان
P.K. Siwach, Pankaj Srivastava, H.K. Singh, A. Asthana, Y. Matsui, T. Shripathi, O.N. Srivastava,