کد مقاله | کد نشریه | سال انتشار | مقاله انگلیسی | نسخه تمام متن |
---|---|---|---|---|
1881878 | 1533448 | 2008 | 4 صفحه PDF | دانلود رایگان |
LiAlO2:Mn/CeLiAlO2:Mn/Ce phosphor was prepared by combustion synthesis. LiAlO2:MnLiAlO2:Mn exhibits two thermoluminescence (TL) peaks around 150 and 320∘C while LiAlO2:CeLiAlO2:Ce exhibits TL peaks around 170 and 280∘C. PL emission of LiAlO2:MnLiAlO2:Mn consists of a peak around 500 nm when excited with 450 nm while LiAlO2:CeLiAlO2:Ce shows a broad band around 400 nm when excited by 320 nm. The TL emission spectrum of LiAlO2:MnLiAlO2:Mn consists of a broad band at 500 nm attributed to the T14 to A16 transitions of Mn2+Mn2+ ion, indicating that Mn2+Mn2+ is the luminescence centre in LiAlO2:MnLiAlO2:Mn.ESR studies were carried out to identify defect centres responsible for TL peaks observed in LiAlO2:CeLiAlO2:Ce. Room temperature ESR spectrum of irradiated LiAlO2:CeLiAlO2:Ce phosphor appears to be superposition of at least four distinct centres. Two defect centres (centres I and II) are identified in irradiated LiAlO2:CeLiAlO2:Ce phosphor and these centres are assigned to O-O- and F+F+ centres, respectively. O-O- centre appears to correlate with the 170∘C TL peak and F+F+ centre appears to correlate with both 170 and 280∘C TL peaks in LiAlO2:CeLiAlO2:Ce.
Journal: Radiation Measurements - Volume 43, Issues 2–6, February–June 2008, Pages 291–294