Pure K0.5Na0.5NbO3 powders were prepared at low temperatures by an efficient method using Na2CO3, K2CO3 and Nb2O5 as raw materials and urea as fuel. The phase evolution of the powders was investigated by X-ray diffractometer (XRD) and thermo gravimetric analysis-differential scanning calorimeter (TG–DSC). The phase composition and morphology of the powders were characterized by electron probe microanalysis (EPMA) and scanning electron microscope (SEM), respectively. The results reveal that single-phase K0.5Na0.5NbO3 powder can be obtained at 550 °C by the method. The as-prepared powder is stoichimetric, fine and well-developed.
Pure K0.5Na0.5NbO3 powder was firstly prepared at low temperature by an efficient method using Na2CO3, K2CO3 and Nb2O5 as raw materials and urea as fuel. From the following figure, it can be found that the pure KNN powders can be prepared by the low-temperature combustion method at 550 °C, which is far lower than the temperature prepared by conventional solid-state temperature.Figure optionsDownload as PowerPoint slide
Journal: Powder Technology - Volume 196, Issue 2, 10 December 2009, Pages 233–236