ZnOmaterial has unique electrical and optical properties that many important applications, including as an anti-reflection coating in dye sensitized solar cells. Flat anti-reflective coatings (ARC) made of ZnO on top to improve the optical properties of the coating. In this study, ZnO nanoparticle were coated with TiO2 nanolayers by a simple wet chemical route. TiO2 nanorods coated ZnO nanoparticle was synthesized by two step i.e. (1) base hydrolysis and polymerization of TiO2 (2) ZnO nanoparticle were coated with a TiO2 layer. The TiO2 coated ZnO prepared was characterized by X-ray diffraction (XRD), Reflectance spectroscopy, SEM and TEM. ZnO annealed at a temperature of 400oC have the greatest crystal size than annealedat a temperature of 500 °C and 600 °C. While, the Reflectance (%R)properties shows that the higher annealing temperature of ZnO preparations, the higher of %R value of ZnO thin layer. The ZnO prepared by annealed at 400oCgain a good performance of the lowest reflectance value. The difference properties are due to differences of light scattering resulting from the crystal size effect. The crystals size that have a good performance as an anti-reflection is around 20 nm, result study of ZnOannealed at 400 °C. TEM nanograph shows that the synthesized ZnO have spherical morphology. The optimum performance ofDSSCs was conducted using the photoanode ZnO-coated TiO2at present 10%APTMS as surface modifier anchor dye group. Bythe addition of ARC we have been capable improve cell performance so that cells achieve an efficiency of 1.13%.
Journal: Procedia Chemistry - Volume 19, 2016, Pages 632-637