Improvement on mechanical properties and wear resistance of HVOF sprayed WC-12Co coatings by optimizing feedstock structure
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
شیمی
شیمی تئوریک و عملی
پیش نمایش صفحه اول مقاله

چکیده انگلیسی
WC-12Co powders with a bimodal size distributed WC particles were used to produce coating by high velocity oxy-fuel (HVOF) spraying (B coating), and HVOF sprayed WC-12Co coatings from microstructured, submicrostructured and nanostructured powders were also fabricated for comparison. The phase constitution, microstructure, mechanical properties and wear performance of the coatings were investigated. Decarburization occurred during coatings preparation, and the carbide retention of B coating was 0.934, higher than that of nanostructured coating. B coating exhibited typical multimodal microstructure, and had considerably high microhardness and the highest fracture toughness among the four coatings, with the values of 1291 HV0.1 and 10.76 MPa m1/2, respectively. When sliding against GCr15 ring in block-on-ring configuration, B coating exhibited the lowest wear rate and relatively lower friction coefficient compared with other coatings, with the average values of 0.94 Ã 10â7 mm3 Nâ1 mâ1 and 0.63 at 245 N load, respectively, which could be attributed to the concrete-like structure.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Applied Surface Science - Volume 320, 30 November 2014, Pages 364-371
Journal: Applied Surface Science - Volume 320, 30 November 2014, Pages 364-371
نویسندگان
Ning Ma, Lei Guo, Zhenxiong Cheng, Huantao Wu, Fuxing Ye, Keke Zhang,