Surface integrity after pickling and anodization of Ti-6Al-4V titanium alloy

No significant changes of the equiaxe microstructure were detected between sample core and surface, or after the pickling and anodization steps. Surface hydrogen and oxygen superficial contents were found to remain unchanged. Roughness characteristics (i.e. Ra, Rz but also local Kt factor) similarly showed only slight modifications, although SPM and SEM revealed certain random local surface defaults, i.e. pits about 400 nm in depth. Finally internal stresses, evaluated using X-ray diffraction, highlighted a significant decrease of the compressive internal stresses, potentially detrimental for fatigue resistance.