Multi-layer graphene oxide alone and in a composite with nanosilica: Preparation and interactions with polar and nonpolar adsorbates

- Textural characteristics of MLGO are affected by dispersion medium and adsorbates.
- O-functionalized carbon sheets strongly interact in MLGO stacks.
- Freezing-melting hysteresis is observed for both polar and nonpolar adsorbates bound to MLGO.

Freeze-dried multi-layer graphene oxide (MLGO), produced from natural flake graphite using ionic hydration method, demonstrates strong interactions of functionalized carbon sheets with polar or nonpolar adsorbates or co-adsorbates depending on the characteristics of dispersion media. Interactions of MLGO with a mixture of water and n-decane in chloroform media provide specific surface area (Su) in contact with unfrozen liquids greater than 1000 m2/g corresponding to stacks with 3-5 carbon layers. Electrostatic interactions between functionalized carbon sheets in dried MLGO are very strong. Therefore, nonpolar molecules (benzene, decane, nitrogen) cannot penetrate between the sheets. Water molecules can effectively penetrate between the sheets, especially if MLGO is located in weakly polar CDCl3 medium. In this case, n-decane molecules (co-adsorbate) can also penetrate into the sheet stacks and locate around nonpolar fragments of the sheets. The Su value of MLGO being in contact with unfrozen water can reach 360 m2/g, but upon co-adsorption of water with decane Su = 930 m2/g, i.e., hydrophobic interactions of the mentioned fragments with decane are stronger that with co-adsorbed water. Water alone (0.25 or 0.5 g/g) bound to MLGO in a mixture with fumed silica A-300 in air or CDCl3 media can provide Su = 30-50 m2/g. Pores in wetted MLGO or MLGO/A-300 mainly correspond to mesopores. Nanosilica does not provide significant opening of the MLGO sheet stacks during their mechanical mixing.

Multi-layer graphene oxide alone and in a composite with nanosilica: preparation and interactions with polar and nonpolar adsorbates.276