Effect of alkaline cleaning and activation on aluminum alloy 7075-T6
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
شیمی
شیمی تئوریک و عملی
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
The effect of alkaline cleaning and activation on the composition and thickness of the oxide layer on aluminum alloy 7075-T6 was studied. E-pH diagrams were developed to predict the effect of alkaline cleaning and activation solutions on the stability of the oxide surface layers. The thickness of the native oxide layer was determined to be â¼30Â nm by Auger electron spectroscopy depth profiling analysis. The outer â¼20Â nm was rich in magnesium while the remaining â¼10Â nm was rich in aluminum. Cleaning in a 9.1 pH alkaline solution was found to remove the magnesium-rich layer and leave behind an aluminum-rich oxide layer â¼10Â nm thick. Activation in alkaline solutions of NaOH (pHÂ >Â 12.9) or Na2CO3 (pHÂ >Â 11.5) produced an oxide that was â¼20 to 60Â nm thick and rich in magnesium. Alkaline cleaning and activation altered the oxide composition and thickness making it possible for deposition of thicker cerium-based conversion coatings (â¼100 to 250Â nm) compared to only alkaline cleaning (â¼30Â nm), with application of one spray cycle of deposition solution.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Applied Surface Science - Volume 257, Issue 6, 1 January 2011, Pages 1859-1863
Journal: Applied Surface Science - Volume 257, Issue 6, 1 January 2011, Pages 1859-1863
نویسندگان
Simon Joshi, William G. Fahrenholtz, Matthew J. O'Keefe,