Non-silicon substrate bonding mediated by poly(dimethylsiloxane) interfacial coating

- Non-silicon thermoplastic was bonded with poly(dimethylsiloxane) silicone elastomer.
- Low-molecular-weight PDMS interfacial layer was chemically coated on thermoplastic.
- Bonding was realized by corona treatment and physical contact under ambient condition.
- Bonding is universally applicable regardless of thermoplastic type and property.
- Homogeneous PDMS-like microchannel was obtained inside the thermoplastic-PDMS microdevice.

In this paper, we introduce a simple and robust strategy for bonding poly(dimethylsiloxane) (PDMS) with various thermoplastic substrates to fabricate a thermoplastic-based closed microfluidic device and examine the feasibility of using the proposed method for realizing plastic-plastic bonding. The proposed bonding strategy was realized by first coating amine functionality on an oxidized thermoplastic surface. Next, the amine-functionalized surface was reacted with a monolayer of low-molecular-weight PDMS, terminated with epoxy functionality, by forming a robust amine-epoxy bond. Both the PDMS-coated thermoplastic and PDMS were then oxidized and permanently assembled at 25 °C under a pressure of 0.1 MPa for 15 min, resulting in PDMS-like surfaces on all four inner walls of the microchannel. Surface characterizations were conducted, including water contact angle measurement, X-ray photoelectron spectroscopy (XPS), and fluorescence measurement, to confirm the successful coating of the thin PDMS layer on the plastic surface, and the bond strength was analyzed by conducting a peel test, burst test, and leakage test. Using the proposed method, we could successfully bond various thermoplastics such as poly(methylmethacrylate) (PMMA), polycarbonate (PC), polystyrene (PS), and poly(ethylene terephthalate) (PET) with PDMS without the collapse or deformation of the microchannel, and the proposed method was successfully extended to the bonding of two thermoplastics, PMMA, and PC.

Low-molecular-weight PDMS coating on the surfaces of non-silicon substrates such as thermoplastics ensures permanent sealing with a silicone elastomer, PDMS, simply by surface oxidization followed by ambient condition bonding, mediated by a robust siloxane bond formation at the interface.