Structure, tribological and electrochemical properties of low friction TiAlSiCN/MoSeC coatings
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
شیمی
شیمی تئوریک و عملی
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Structure, tribological and electrochemical properties of low friction TiAlSiCN/MoSeC coatings Structure, tribological and electrochemical properties of low friction TiAlSiCN/MoSeC coatings](/preview/png/5357590.png)
چکیده انگلیسی
The present paper is focused on the development of hard tribological coatings with low friction coefficient (CoF) in different environments (humid air, distilled water) and at elevated temperatures. TiAlSiCN/MoSeC coatings were deposited by magnetron sputtering of four-segment targets consisting of quarter circle TiAlSiCN segments, obtained by self-propagating high-temperature synthesis, and one or two cold pressed segments made of MoSe2 and C powders in a ratio 1:1 wt%. The structure and phase composition of coatings were investigated by means of X-ray diffraction, transmission electron microscopy, X-ray photoelectron spectroscopy, and Raman spectroscopy. The coatings were characterized in terms of their hardness, elastic modulus, and elastic recovery. The tribological properties of coatings were investigated first at room temperature against Al2O3 and WC-Co balls, after which studied in distilled water and during continuous heating in air in the temperature range of 25-400 °C against Al2O3 counterpart material. To evaluate their electrochemical characteristics, the coatings were tested in 1 N H2SO4 solution. The obtained results show that the coating hardness depends on the amount of MoSeC additives and decreased from 40 to 28 (one MoSeC segment) and 12 GPa (two MoSeC segments). Doping with MoSeC resulted in a significant reduction of CoF values measured in humid air (RH 60 ± 5%) from 0.8-0.9 to 0.05 and an increase of wear resistance by one or two orders of magnitude depending on counterpart material. This was attributed to the presence of MoSe2 and free carbon-based phases in the tribological contact. The TiAlSiCN/MoSeC coating with a maximal amount of MoSeC also demonstrated superior tribological characteristics in distilled water (CoF â¼Â 0.1) and at moderate temperatures up to 300 °C (CoF < 0.1). The electrochemical tests showed that, in general, doping with MoSeC did not negatively affect the coating electrochemical behavior. On the contrary, the MoSeC phase demonstrated small positive effect on the anti-corrosive properties of TiAlSiCN coatings under small polarizations.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Applied Surface Science - Volume 327, 1 February 2015, Pages 253-261
Journal: Applied Surface Science - Volume 327, 1 February 2015, Pages 253-261
نویسندگان
A.V. Bondarev, Ph.V. Kiryukhantsev-Korneev, A.N. Sheveyko, D.V. Shtansky,