Pt catalysts on PANI coated WC/C nanocomposites for methanol electro-oxidation and oxygen electro-reduction in DMFC

In the present study a Pt/PANI/WC/C electrocatalyst was developed to increase the methanol electro-oxidation and oxygen electro-reduction activity and stability of commercial Pt/C electrocatalyst. WC/C was coated with protonated polyaniline (PANI) in situ during the polymerization of aniline. Fourier transform infrared (FTIR) results illustrate the presence of PANI in the composite. The conductivity of PANI coated - WC/C has been compared with the conductivity of the corresponding mixtures of WC/C and Vulcan XC-72. X-ray diffraction results showed that Pt particles were dispersed on the support with mean particle size of about 10.56 nm. Transition electron microscopy images showed that the nanosized WC/C were successfully coated by PANI. Based on the electrochemical properties characterized by cyclic voltammetry, CO stripping and rotating disk electrode measurements it was found that the as prepared Pt/PANI/WC/C electrocatalyst exhibited a comparable activity for methanol oxidation reaction and oxygen reduction reaction with respect to the commercial one. A significant reduction in the potential of CO electro-oxidation peak from 0.75 V for Pt/C to 0.52 V for Pt/PANI/WC/C electrocatalyst indicates that an increase in the activity for CO electro-oxidation is achieved by replacing the carbon support by PANI coated WC/C. Chronoamerometry results also showed, in the presence of methanol the Pt/PANI/WC/C electrocatalyst still maintains a higher current density than Pt/WC/C and Pt/C.