Mesoporous titania-alumina mixed oxide: A preliminary study on synthesis and application in selective catalytic reduction of NOx
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
شیمی
شیمی تئوریک و عملی
پیش نمایش صفحه اول مقاله

چکیده انگلیسی
Titania-alumina mixed oxide was synthesized hydrothermally using tetrapropylammonium hydroxide (TPAOH) as the template. The dried, calcined and palladium loaded samples were characterized for particle morphology, weight loss, nitrogen adsorption/desorption at liquid nitrogen temperature, texture and metal dispersion. The Pd loaded material was tested for NO reduction in a fixed bed catalytic reactor using a simulated gas mixture closely resembling lean burn engine exhaust. Scanning electron microscopy of the dried and calcined samples revealed a well developed tubular fibrous network of titania-alumina. Thermogravimetry (TG) of the dried sample indicated about 16% weight loss due to decomposition of an oxy-hydroxide structure of the material, mostly boehmite, which was confirmed by X-ray diffraction (XRD) measurements. The boehmite phase changed to poorly crystalline γ-alumina upon calcination where as titania remained as anatase. BET specific surface area, adsorption-desorption isotherms and BJH pore size distributions indicated formation of a mesoporous structure. The surface area of the dried material increased when calcined at 600 °C but the pore size distribution patterns for the dried, calcined and palladium dispersed materials remained unchanged. These observations along with TG and XRD analyses suggest that a thermo-resistant, mesoporous, high surface area, crystalline titania-alumina framework can be prepared using the hydrothermal synthesis route. A peak NOx conversion of 75% with the palladium dispersed catalyst indicates high catalytic activity, possibly due to high dispersion of Pd confirmed by CO chemisorption studies.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Applied Surface Science - Volume 254, Issue 21, 30 August 2008, Pages 7098-7103
Journal: Applied Surface Science - Volume 254, Issue 21, 30 August 2008, Pages 7098-7103
نویسندگان
H.K. Mishra, M. Stanciulescu, J.-P. Charland, J.F. Kelly,