Structural morphology study of Cd2+ induced Langmuir Blodgett multilayer films of arachidic acid

The organization and headgroup co-ordination of Cadmium Arachidate (CdAA) molecule in Langmuir-Blodgett (LB) multilayer films deposited on hydrophilic Glass (SiO2) and Silicon (100) substrate at normal subphase pH (6.8) are studied. X-ray diffraction (XRD) and X-ray reflectivity (XRR) study reveals ordered layer by layer organization with uniform packing of CdAA molecules, and with a small tilt angle of alkyl chain of CdAA molecule equal to 6.8° ± 1.75°. Electron density profiles (EDPs) shows that the coverage of films remains almost constant with increase in bilayer thickness which indicate very little presence of pinhole defects. AFM study for 25 ML shows that coverage of the film remain intact upto 22nd ML and then decreases sharply due to presence of pinhole defects. Fourier transform infrared spectroscopy (FTIR) study is also consistent with XRD and XRR study of ordered deposition of CdAA molecule. FTIR and X-ray photoelectron spectroscopy (XPS) study indicates the formation of unidentate bridging metal-carboxylate coordination type headgroups consistent with one cadmium metal ion between two carboxylate (COO) groups in each headgroup structure.

► Well defined pattern deposition of CdAA molecules with uniform packing. ► Tilting occurs in long chain fatty acids synthesized by LB method. ► Pinhole defects presence was seen minimal upto 21st monolayer in LB prepared CdAA fatty acid films at pH ∼6.8. ► FTIR and XPS study indicates the formation of unidentate bridging metal-carboxylate coordination.