Oxygen plasma functionalization of poly(p-phenilene sulphide)
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
شیمی
شیمی تئوریک و عملی
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Oxygen plasma functionalization of poly(p-phenilene sulphide) Oxygen plasma functionalization of poly(p-phenilene sulphide)](/preview/png/5364033.png)
چکیده انگلیسی
Surface effects during plasma activation of poly(p-phenilene sulphide)-PPS have been studied. Samples that were exposed to weakly ionized highly dissociated oxygen plasma created an inductively coupled radiofrequency discharge with the power of 100Â W. The electron density and temperature were measured with a double Langmuir probe and were 4Â ÃÂ 1015Â mâ3 and 3Â eV, respectively, while the neutral atom density was measured with a fiber optics catalytic probe and was 4Â ÃÂ 1021Â mâ3. The surface tension was determined by measuring the contact angle of deionized water, while the appearance of surface functional groups was detected by XPS. The surface tension of untreated PPS was 7Â ÃÂ 10â3Â N/m or/and increased to 7Â ÃÂ 10â2Â N/m in few seconds of plasma treatment. It remained fairly constant for longer plasma treatments. The XPS survey spectrum showed little oxygen on untreated samples, but its concentration increased to about 20Â at.% in few seconds. Detailed high resolution XPS C 1s peak showed that the carbon was left fairly stable during plasma treatment. The main functional groups formed were rather sulphate in sulphite groups, as determined from high resolution S 2p peak. Namely, a strong transition from sulphide to sulphate state of sulfur was observed. The spontaneous deactivation of the polymer surface was measured as well. The deactivation was fairly logarithmic with the characteristic decay time of several hours.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Applied Surface Science - Volume 253, Issue 21, 31 August 2007, Pages 8669-8673
Journal: Applied Surface Science - Volume 253, Issue 21, 31 August 2007, Pages 8669-8673
نویسندگان
UroÅ¡ Cvelbar, Miran MozetiÄ, Ita Junkar, Alenka Vesel, Janez KovaÄ, Aleksander Drenik, TjaÅ¡a VrliniÄ, Nina Hauptman, Marta KlanjÅ¡ek-Gunde, BoÅ¡tjan Markoli, NikÅ¡a KrstuloviÄ, Slobodan MiloÅ¡eviÄ, Freddy Gaboriau, Thierry Belmonte,