Na-doped hydroxyapatite coating on carbon/carbon composites: Preparation, in vitro bioactivity and biocompatibility

Na-doped hydroxyapatite (Na-HA) coating was directly prepared onto carbon/carbon (C/C) composites using electrochemical deposition (ECD) and the mean thickness of the coating is approximately 10 ± 2 μm. The formed Na-HA crystals which are Ca-deficient, are rod-like with a hexagonal cross section. The Na/P molar ratios of the coating formed on C/C substrate is 0.097. During the deposition, the Na-HA crystals grow in both radial and longitudinal directions, and faster along the longitudinal direction. The pattern formation of crystal growth leads to dense coating which would help to increase the bonding strength of the coating. The average shear bonding strength of Na-HA coating on C/C is 5.55 ± 0.77 MPa. The in vitro bioactivity of the Na-HA coated C/C composites were investigated by soaking the samples in a simulated body fluid (SBF) for 14 days. The results indicate that the Na-HA coated C/C composites can rapidly induce bone-like apatite nucleation and growth on its surface in SBF. The in vitro cellular biocompatibility tests reveal that the Na-HA coating was better to improve the in vitro biocompatibility of C/C composites compared with hydroxyapatite (HA) coating. It was suggested that the Na-HA coating might be an effective method to improve the surface bioactivity and biocompatibility of C/C composites.

► Na-HA coating with a thickness of 10 ± 2 μm was directly prepared onto C/C using ECD. ► The shear bonding strength of Na-HA coating on C/C is 5.55 ± 0.77 MPa. ► Na-HA coated C/C can rapidly induce bone-like apatite nucleation and growth on its surface in SBF. ► The Na-HA coating was better to improve the biocompatibility of C/C compared with HA coating.