![عکس صفحه اول مقاله: Irradiation of the graphite-like carbon films by ns-laser pulse Irradiation of the graphite-like carbon films by ns-laser pulse](/preview/png/5364571.png)
The effect of a nanosecond laser irradiation of graphite-like carbon (GLC) films deposited on Si substrate by the plasma jet technique was analyzed in this work. The GLC coatings were irradiated by the nanosecond Nd:YAG lasers operating at 1064Â nm (infrared (IR) radiation) and 532Â nm (visible (VIS) radiation), using a multi-shot regime. The laser irradiations lead to the surface ablation and partial disarrangement of the GLC coatings. The IR laser irradiation stimulates an increase in the fraction of the sp2 carbon bonds and formation of the nano-graphite cluster. The formation of SiC and graphite nanocrystallites was observed after VIS laser radiation by 24Â MW/cm2 energy density. FTIR results demonstrated that the reflectance of the laser irradiated carbon films decreases.
⺠The ns-laser irradiation leads to the surface ablation and partial disarrangement of the graphite-like carbon coatings. ⺠The laser irradiation increases the fraction of the sp2 carbon sites and lead to the formation nano-graphite structure. ⺠The GLC films reflectance decreases after laser irradiation.
Journal: Applied Surface Science - Volume 261, 15 November 2012, Pages 488-492