ZrC/ZrB2 multilayered coatings with bilayer periods ranging from 4.4 to 35.5Â nm were synthesized by r.f. magnetron sputtering. X-ray diffraction, scanning electron microscopy and nanoindention were employed to investigate the microstructure and mechanical properties of the nanoscale multilayers. The results indicated that all coatings had the clear multilayered structure with mixed ZrB2(0Â 0Â 1), ZrB2(0Â 0Â 2) and ZrC(1Â 1Â 1) preferred orientations. The maximum hardness (41.7Â GPa) was observed in the multilayer with 27.5-nm thick period, which is about 25% higher than the rule-of-mixture value of the monolithic ZrC and ZrB2 coatings. It also exhibited the best adhesion. Its critical load was over 70Â mN. While through insert ZrB2 into ZrC layer periodically, higher residual stress built in ZrC layer can be released.
Journal: Applied Surface Science - Volume 253, Issue 12, 15 April 2007, Pages 5302-5305