![عکس صفحه اول مقاله: Enhanced corrosion resistance of mild steel in molar hydrochloric acid solution by 1,4-bis(2-pyridyl)-5H-pyridazino[4,5-b]indole: Electrochemical, theoretical and XPS studies Enhanced corrosion resistance of mild steel in molar hydrochloric acid solution by 1,4-bis(2-pyridyl)-5H-pyridazino[4,5-b]indole: Electrochemical, theoretical and XPS studies](/preview/png/5367159.png)
The inhibition effect of the new pyridazine derivative, namely 1,4-bis(2-pyridyl)-5H-pyridazino[4,5-b]indole (PPI) against mild steel corrosion in 1Â M HCl solutions was evaluated using weigh loss and electrochemical techniques (potentiodynamic polarisation curves and impedance spectroscopy). The experimental results suggest that PPI is a good corrosion inhibitor and the inhibition efficiency increased with the increase of PPI concentration, while the adsorption followed the Langmuir isotherm. X-ray photoelectron spectroscopy (XPS) and theoretical calculation of electronic density were carried out to establish the mechanism of corrosion inhibition of mild steel with PPI in 1Â M HCl medium. The inhibition action of this compound was, assumed to occur via adsorption on the steel surface through the active centres contained of the molecule. The corrosion inhibition is due to the formation of a chemisorbed film on the steel surface.
Journal: Applied Surface Science - Volume 252, Issue 8, 15 February 2006, Pages 2684-2691