Growth of Fe on Ge(1 1 1) at room temperature studied by X-ray photoelectron diffraction

The growth of ultrathin Fe films of various coverages on Ge(1 1 1) at room temperature using molecular beam epitaxy (MBE) was studied via X-ray photoelectron diffraction (XPD or XPED) together with low energy electron diffraction (LEED) and X-ray photoelectron spectroscopy (XPS). All experimentally observed XPD patterns suggested local order structures of the Fe layers for all thicknesses studied. The short-range order of the resulting structures was found to be enhanced for thinner layers whereas the long-range order was gradually lost with increasing Fe thicknesses. At a very low coverage of 0.8 Å Fe and Ge tend to react to the partly ordered structure in which Fe atoms were located in local environments similar to those for higher Fe coverages. Comparison of theoretical and experimental XPD patterns, along with XPS results, showed that intermixing between Fe and Ge occurred during the pseudomorphic growth with a stacking fault near the interface for all Fe coverages under study. Nevertheless, small percentage of domains without the stacking fault was also found to coexist with those with the stacking fault by performing a quantitative analysis of a reliability factor R of the Fe2p pattern for 5.4 Å. The orientation changes of the Ge2p and Ge3d XPD patterns with Fe thickness were unambiguously explained in terms of their different dependencies on the overlayer thickness due to the different inelastic mean free path lengths used in the simulations. Also, Fe got increasingly enriched in the grown layers with increased Fe coverage. The resulting structures and intermixing are discussed in detail.