Solubility limit of Si in YAG at 1700 °C in vacuum
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
سرامیک و کامپوزیت
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
Measurement of the solubility limit of Si in yttrium aluminum garnet (YAG-Y3Al5O12) is crucial for understanding the mechanisms by which Si influences grain boundary mobility, and the mechanisms by which grain boundaries migrate. In the present work, the solubility limit of Si in YAG at 1700 °C in vacuum (5 Ã 10â6 Torr), which are the most common sintering temperature and environment for YAG, was measured for the first time. Measurements were conducted by wavelength dispersive spectroscopy (WDS), using polished YAG specimens with 3700 ppm Si (0.8 wt% SiO2). Si content to ensure saturation with Si. The accuracy of the WDS result was confirmed by using a series of doped specimens and by comparing to inductively coupled plasma mass spectrometry ICP-MS results. The results indicate that the solubility limit of Si in YAG at 1700 °C (5 Ã 10â6 Torr), is 980 ± 60 ppm. The measured Si solubility was found to significantly depend on the cooling rate, where for furnace cooled specimens the measured Si solubility was 650 ± 60 ppm. A second phase in triple junction was repeatedly observed when higher content of Si was used, confirming this work results.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of the European Ceramic Society - Volume 37, Issue 1, January 2017, Pages 243-248
Journal: Journal of the European Ceramic Society - Volume 37, Issue 1, January 2017, Pages 243-248
نویسندگان
Shlomit Zamir,