Photoluminescence properties of Tb3Al5O12:Ce3+ garnet synthesized by the metal organic decomposition method

Tb3Al5O12:Ce3+ garnet (TAG:Ce3+) phosphor was synthesized by the metal organic decomposition (MOD) method and subsequent calcination at Tc = 800-1200°C for 1 h in air. The effects of Ce3+ concentration on the phosphor properties were investigated in detail using X-ray diffraction (XRD) analysis, photoluminescence (PL) analysis, PL excitation (PLE) spectroscopy, and PL decay measurements. The maximum intensity in the Ce3+ yellow emission was observed at the Ce3+ concentration of ∼0.20%. PLE and PL decay measurements suggested an evidence of the energy transfer from Tb3+ to Ce3+. Calcination temperature dependence of the XRD and PL intensities yielded an energy of ∼1.5 eV both for the TAG formation in the MOD process and for the optical activation of Ce3+ in its lattice sites. Temperature dependences of the PL intensity for the TAG:Ce3+ yellow-emitting and K2SiF6:Mn4+ red-emitting phosphors were also examined for the future solid-state lighting applications at T = 20-500 K in 10-K steps. The data of TAG:Ce3+ were analyzed using a theoretical model with considering a reservoir level of Et ∼9 meV, yielding a quenching energy of Eq ∼0.35 eV, whereas the K2SiF6:Mn4+ red-emitting phosphor data yielded a value of Eq ∼1.0 eV. The schematic energy-level diagrams for Tb3+ and Ce3+ were proposed for the sake of a better understanding of these ions in the TAG host.