عنوان انگلیسی مقاله ISI
A study of long-term static load on degradation and mechanical integrity of Mg alloys-based biodegradable metals
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
مواد الکترونیکی، نوری و مغناطیسی
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: A study of long-term static load on degradation and mechanical integrity of Mg alloys-based biodegradable metals A study of long-term static load on degradation and mechanical integrity of Mg alloys-based biodegradable metals](/preview/png/5448805.png)
چکیده انگلیسی
Predicting degradation behavior of biodegradable metals in vivo is crucial for the clinical success of medical devices. This paper reports on the effect of long-term static stress on degradation of magnesium alloys and further changes in mechanical integrity. AZ31B (H24) and ZE41A (T5) alloys were tested to evaluate stress corrosion cracking (SCC) in a physiological solution for 30Â days and 90Â days (ASTM G39 testing standard). Scanning electron microscopy (SEM) with energy-dispersive X-ray spectroscopy (EDX) and micro-computed tomography (micro-CT) were used to characterize surface morphology and micro-structure of degraded alloys. The results show the different mechanisms of stress corrosion cracking for AZ31B (transgranular stress corrosion cracking, TGSCC) and ZE41A (intergranular stress corrosion cracking, IGSCC). AZ31B was more susceptible to stress corrosion cracking under a long term static load than ZE41A. In conclusion, we observed that long-term static loading accelerated crack propagation, leading to the loss of mechanical integrity.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Science and Engineering: B - Volume 219, May 2017, Pages 45-54
Journal: Materials Science and Engineering: B - Volume 219, May 2017, Pages 45-54
نویسندگان
Youngmi Koo, Yongseok Jang, Yeoheung Yun,