Effects of Ni content on low cycle fatigue and mechanical properties of Al-12Si-0.9Cu-0.8Mg-xNi at 350 °C
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
دانش مواد (عمومی)
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
In order to study the effects of ε-Al3Ni phase on elevated temperature properties, Al-12Si-0.9Cu-0.8Mg-xNi alloys with Ni contents of 1.0%, 2.5% and 4.0%, respectively, were prepared by gravity casting and their microstructure, tensile and low cycle fatigue properties at 350 °C were investigated. The results show that the microstrucure mainly consists of α-Al, eutectic Si, ε-Al3Ni, δ-Al3CuNi, and Q-Al5Cu2Mg8Si6 phase. Thermodynamic calculation indicates that the ε-Al3Ni weight fraction increases with Ni contents while other phase contents are kept constant, and this result is consistent with the microstructure and XRD analysis. With the increase of ε-Al3Ni content, the tensile strength at 350 °C increases from 94 MPa to 116 MPa, while the elongation decreases from 2.8% to 2.0%. The Al-Si alloy with 2.5% Ni exhibits the optimal low cycle fatigue property with a fatigue strength coefficient of 198.29 MPa and fatigue strength exponent of â 0.1295. The coarsening of ε-Al3Ni phase is obvious with a higher Ni content of 4.0%, and the debonding of coarse ε-Al3Ni phase accelerates the propagation of micro-cracks and degrades the fatigue properties. The ε-Al3Ni phase is beneficial to the mechanical properties of the alloys and thermally stable during fatigue test at 350 °C.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Science and Engineering: A - Volume 706, 26 October 2017, Pages 27-37
Journal: Materials Science and Engineering: A - Volume 706, 26 October 2017, Pages 27-37
نویسندگان
Jian Feng, Bing Ye, Lijie Zuo, Ruijuan Qi, Qudong Wang, Haiyan Jiang, Rong Huang, Wenjiang Ding,