Characterization of fracture in medium Mn steel
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
دانش مواد (عمومی)
پیش نمایش صفحه اول مقاله

چکیده انگلیسی
Three mechanisms contributed to the damage that developed in these materials. First, nucleation and growth of voids occurred at non-metallic inclusions. Second, debonding of the α-αⲠand αâ²-αⲠinterfaces due to a local loss of interfacial strength was observed in the UFG constituent. While the voids initiated at non-metallic inclusions were in the order of several microns, the size of those initiated at the α-αⲠand αâ²-αⲠinterfaces in the UFG constituent was limited by the initial grain size, with little or no growth. Finally, in addition to void damage, longitudinal cleavage-like cracks formed along the δ-ferrite layers, and parallel to the sheet plane, were observed in the fractured specimens. These longitudinal cleavage-like cracks were the consequence, but not the cause, of a fracture process triggered by plastic flow localization during uniaxial tension testing.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Science and Engineering: A - Volume 687, 27 February 2017, Pages 200-210
Journal: Materials Science and Engineering: A - Volume 687, 27 February 2017, Pages 200-210
نویسندگان
Hongki Choi, Seonjong Lee, Jaewook Lee, Frédéric Barlat, Bruno C. De Cooman,