Effects of cryogenic temperature and pre-stretching on mechanical properties and deformation characteristics of a peak-aged AA6082 extrusion
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
دانش مواد (عمومی)
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
Plastic deformation studies of a peak-aged AA6082 alloy by means of tensile tests at 77 K and 295 K, and related microstructure characteristics obtained by Scanning Electron Microscopy (SEM), Electron Backscatter Diffraction (EBSD), Transmission Electron Microscopy (TEM) and Atom Force Microscopy (AFM), revealed new results. A simultaneous improvement in ductility and strength occurred at 77 K, but not at 295 K. A higher work hardening accompanied by a more homogeneous slip mode explained the improved properties at 77 K. Pre-stretching at these two temperatures and subsequent tensile testing at room temperature revealed a marked yield point. However, pre-stretching at 77 K exhibited a slightly higher room temperature yield strength and ductility than the condition pre-stretched at 295 K. Annealing after pre-stretching improved ductility and reduced the magnitude of the yield point. Pre-stretching at 77 K and subsequent annealing introduced somewhat higher strength and ductility as compared to the counterpart pre-stretched at 295 K. The observed mechanical behaviour and associated phenomena were directly linked to microstructure characteristics such as deformation substructure history, slip localization, dislocation density and the precipitate β' /β'' ratio.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Science and Engineering: A - Volume 679, 2 January 2017, Pages 379-390
Journal: Materials Science and Engineering: A - Volume 679, 2 January 2017, Pages 379-390
نویسندگان
Zebing Xu, Hans J. Roven, Zhihong Jia,