Probing specific oxides as potential supports for metal/oxide model catalysts: MgO(111) polar film

The growth of thermally evaporated magnesium oxide thin film on Mo(110) substrate in ultra-high vacuum was studied by means of Auger electron spectroscopy (AES), low-energy electron diffraction (LEED) and work function (WF) measurements. It is shown that at a growth rate of c.a. 0.1 monolayer per minute and the substrate temperature of 600 K the film acquires the MgO(111) structure. This structure begins to form at two monolayers and holds up to six monolayers. At higher thickness the film disorders due to weakening of the ordering effect of the isosymmetric Mo(110) support. Adsorption of CO and H2 on the formed MgO(111) film cooled down to 90 K was studied by means of ultraviolet photoelectron spectroscopy (UPS) and reflection absorption infrared spectroscopy (RAIRS) and compared with in-situ obtained results for CO on Pt(111). Comparison of UPS data of CO on MgO(111) and Pt(111) in combination with RAIRS results reveals quite different bonding mechanisms on the metal and the oxide supports. The main feature of CO on MgO(111) is quite high intensity of CO stretch vibration, considerably exceeding that on amorphous MgO, and comparable to that of CO on Pt(111). This is presumably due to the electrostatic effect of the uncompensated microscopic dipole moment of ultrathin MgO(111) film on the enhancing of CO dynamical dipole moment. Adsorption of H2 dramatically reduces the CO stretch intensity as a possible result of removing of dipole moment of MgO(111) surface by hydrogen and (CO+H2) interaction.