عنوان انگلیسی مقاله ISI
Effect of ball-milling time on structural characteristics and densification behavior of W-Cu composite powder produced from WO3-CuO powder mixtures
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
فلزات و آلیاژها
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Effect of ball-milling time on structural characteristics and densification behavior of W-Cu composite powder produced from WO3-CuO powder mixtures Effect of ball-milling time on structural characteristics and densification behavior of W-Cu composite powder produced from WO3-CuO powder mixtures](/preview/png/5457850.png)
چکیده انگلیسی
Understanding the microstructure of W-Cu nanocomposite powder is essential for elucidating its sintering mechanism. In this study, the effect of milling time on the structural characteristics and densification behavior of W-Cu composite powders synthesized from WO3-CuO powder mixtures was investigated. The mixture of WO3 and CuO powders was ball-milled in a bead mill for 1 h and 10 h followed by reduction by heat-treating the mixture at 800 °C in H2 atmosphere with a heating rate of 2 °C/min to produce W-Cu composite powder. The microstructure analysis of the reduced powder obtained by milling for 1 h revealed the formation of W-Cu powder consisting of W nanoparticle-attached Cu microparticles. However, Cu-coated W nanocomposite powder consisting of W nanoparticles coated with a Cu layer was formed when the mixture was milled for 10 h. Cu-coated W nanopowder exhibited an excellent sinterability not only in the solid-phase sintering stage (SPS) but also in the liquid-phase sintering stage (LPS). A high relative sintered density of 96.0% was obtained at 1050 °C with a full densification occurring on sintering the sample at 1100 °C. The 1 h-milled W-Cu powder exhibited a high sinterability only in the LPS stage to achieve a nearly full densification at 1200 °C.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: International Journal of Refractory Metals and Hard Materials - Volume 65, June 2017, Pages 39-44
Journal: International Journal of Refractory Metals and Hard Materials - Volume 65, June 2017, Pages 39-44
نویسندگان
Sung-Soo Ryu, Hae-Ryong Park, Young Do Kim, Hyun Seon Hong,