The rectification of mono- and bivalent ions in single conical nanopores

The polyethylene terephthalate (PET) films were irradiated with single 6.9 MeV/u 58Ni19+ ions at the Lanzhou Interdisciplinary Heavy Ion Microbeam (LIHIM), and single conical nanopores were produced by asymmetric chemical etching of the latent ion tracks. Then, the current-voltage (I-V) characteristic was measured in LiCl, NaCl, KCl, MgCl2, and CaCl2 solution at different concentrations to study the transport properties of different cations in the single conical nanopores respectively. The measured I-V data showed that the conical nanopores have rectified transportation of these cations at the applied voltage of between +2 V and −2 V. The rectification coefficient γ of the mono- and bivalent ions was determined in their solution of 0.0001-1 M measured at 1 V, the result showed that the rectification coefficient is dependent on the valence of the ions and the electrolyte solution.