Rutherford Backscattering Spectrometry studies of 100Â keV nitrogen ion implanted polypropylene polymer

The effect of nitrogen ion implantation on the structure and composition in polypropylene (PP) polymer has been studied. Implantation was carried out using 100 keV N+ ions at different fluences of 1 × 1015, 1 × 1016 and 1 × 1017 ions cm−2 with beam current density of ∼0.65 μA cm−2. Surface morphological changes in the pre- and post-implanted PP specimens have been studied using Rutherford Backscattering Spectrometry (RBS) and UV-Visible Spectroscopy. The spatial distribution of implantation induced modification in the form of carbonization and dehydrogenation in the near surface region of PP matrix, the projected range, retained dose of implanted nitrogen, the various elements present in the implanted layers and their differential cross-sections have been analyzed using RBS spectra. RUMP simulation yielded an increase in the concentration of carbon near the surface from 33 at.% (virgin) to 42 at.% at fluence of 1 × 1017 N+ cm−2. Further, optical absorption has been found to increase with a shift in the absorption edge from UV towards visible region with increasing fluence. UV-Vis absorption spectra also indicate a drastic decrease in optical energy gap from 4.12 eV (virgin) to 0.25 eV (1 × 1017 N+ cm−2) indicating towards the formation of carbonaceous network in the implanted region. All these changes observed using UV-Visible have been further correlated with the outcomes of the RBS characterization.