Influence of Al content on microstructure, mechanical and tribological properties of Ti-W-Al-N composite films
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
سطوح، پوششها و فیلمها
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Influence of Al content on microstructure, mechanical and tribological properties of Ti-W-Al-N composite films Influence of Al content on microstructure, mechanical and tribological properties of Ti-W-Al-N composite films](/preview/png/5468267.png)
چکیده انگلیسی
Ti-W-Al-N films with various Al content (0 at.% â¼Â 12.4 at.%) were deposited by reactive magnetron sputtering. The composition, microstructure, mechanical and tribological properties of Ti-W-Al-N films were investigated by EDS, XRD, HRTEM, SEM, Nano-indentation, Ball-on-disk tribometer. It is found that Ti-W-Al-N films consist of Ti-W-Al-N phase, Ti2N phase and W2N phase below 2.9 at.% Al. Ti2N phase disappears at 5.6 at.% Al and h-AlN phase forms at 12.4 at.% Al respectively. The hardness firstly increases and then decreases with increasing Al content and the highest hardness is 35.7 GPa at 8.7 at.% Al. At room temperature, the friction coefficient continuously increases, whereas the wear rate firstly decreases and then increases with increasing Al content. The lowest wear rate of 1.79 Ã 10â8 mm3Nâ1mmâ1 is obtained at 8.7 at.% Al. As the temperature increases from room temperature to 700 °C, the friction coefficient firstly increases and then decreases, while the wear rate gradually increases. The tribological properties of the film depended on the testing temperatures significantly because the testing temperatures influenced the hardness, the tribo-films and wear mechanism of the film.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Vacuum - Volume 137, March 2017, Pages 31-37
Journal: Vacuum - Volume 137, March 2017, Pages 31-37
نویسندگان
Lihua Yu, Jian Chen, Hongbo Ju, Hongzhi Dong, Hongjian Zhao,