Investigation of in-house superconducting radio-frequency 9-cell cavity made of large grain niobium at KEK

The first in-house, 9-cell, superconducting radio-frequency cavity made of large grain Nb was fabricated at KEK. Some characteristic techniques were employed for the fabrication that were not used for fine grain (FG) Nb. Even though a penetrated hole was created during electron beam welding, it was successfully repaired and did not affect the cavity performance. The completed cavity then underwent vertical tests (VTs) via several surface treatment processes. A defect that caused quenches was found after a VT at 25 mm from the equator where the typical local grinding machine developed at KEK could not be utilized. A new local grinding machine using a 3D printer was thus developed for the first time, and it completely removed this defect. Finally, the cavity achieved a maximum Q0 value of 3.8×1010 and accelerating gradient of 38 MV/m. The obtained Q0 value is about 1.5 times higher than that for the KEK in-house FG cavity.