LaNiO3 type perovskite was prepared by the “self-combustion” method and was used as catalyst precursor for the methane decomposition reaction at 600 and 700 °C. CH4 conversion reaches 80% at 700 °C and 65% at 600 °C using pure CH4. The yield of CNT and H2 were 2.2 gCNT g−1 h−1 and 8.2 L g−1 h−1 at 700 °C respectively after 4 h of reaction. When the reaction is prolonged to 22 h the catalytic activity decreases but the catalyst is still active, the production of hydrogen reaches 63.5 L (STP) per gram of catalyst and the production of MWCNT was equal to 17 g per gram of catalyst.Multi-wall carbon nanotubes were characterized by X-ray diffraction (XRD), surface area (BET), transmission electron microscopy (TEM), scanning electron microscopy (SEM), thermogravimetric analysis (TGA) and Raman spectroscopy. TEM micrographs showed that MWCNT longer than 20 μm were formed with inner diameters ranging from 5 to 16 nm and outer diameters up to about 40 nm.The results obtained here clearly show that the use of the perovskite LaNiO3 as catalytic precursor is very effective for the simultaneous production of carbon nanotubes and hydrogen.
Journal: Catalysis Today - Volume 149, Issues 3–4, 30 January 2010, Pages 365–371