Influences of MAA on the porous morphology of P(St–MAA) latex particles produced by batch soap-free emulsion polymerization followed by stepwise alkali/acid post-treatment

Soap-free P(St–MAA) latex particles with variable styrene (St)/methacrylic acid (MAA) ratio were synthesized by batch emulsion copolymerization at 70 °C for 7 h, and the particles with porous structure were obtained after stepwise alkali/acid post-treatment. The effects of MAA amount on the particle morphologies after the alkali and the stepwise alkali/acid post-treatments were investigated by transmission electron microscopy (TEM) and scanning electron microscopy (SEM). Results indicated that the alkali-treated latex particles showed anomalous structure with rough surface, and no hollow was clearly identified inside them. When these alkali-treated particles were further treated with acid solution, the particle surface became much smoother, and porous morphology appeared. It was found that when the MAA amount was less than or equal to 4 mol%, no obvious morphological variation was observed; while the latex particles showed clearly porous structure as the MAA amount increased to 6 mol%; with the further increase of MAA amount to 8 mol%, the pore size decreased distinctly.

The amount of MAA intensively influenced the morphology of P(St–MAA) latex particles, and the particles showed different morphology after alkali and stepwise alkali/acid post-treatment.Figure optionsDownload high-quality image (63 K)Download as PowerPoint slide