![عکس صفحه اول مقاله: Interactions and dispersion stability of aluminum oxide colloidal particles in electroless nickel solutions in the presence of comb polyelectrolytes Interactions and dispersion stability of aluminum oxide colloidal particles in electroless nickel solutions in the presence of comb polyelectrolytes](/preview/png/611422.png)
The effect of comb polyelectrolytes on the dispersion stability of colloidal alumina particles in DI water and commercial electroless nickel (EN) solutions was investigated. Adsorption of polyelectrolytes and major EN components onto colloidal alumina was assessed by TGA, chemical analysis, and zeta potential measurements. Zeta potential measurements were made during titrations of comb-polyelectrolyte-stabilized dispersions with EN solutions to full ionic strength for the first time. The compilation of titration curves made with varying amounts of comb polyelectrolytes provides high resolution and novel insight into the particle/surfactant/EN systems. Continuous decrease in particle/EN components surface interactions with the increase in comb polyelectrolyte coverage is observed. Laser diffraction measurements reveal steric stabilization of nano- and submicronmeter alumina dispersions in both DI water and EN solutions with >7 wt% and >2 wt% comb polyelectrolyte, respectively.
Dispersion stability of colloidal alumina particles in electroless nickel solutions is achieved with the aid of comb polyelectrolytes. Zeta potential measurements reveal reduced interactions between the particles and the electroless nickel solutions with the increase in comb polyelectrolyte coverage, and that the nature of dispersion stability is steric.Figure optionsDownload as PowerPoint slide
Journal: Journal of Colloid and Interface Science - Volume 323, Issue 2, 15 July 2008, Pages 293–300