![عکس صفحه اول مقاله: Synthesis, characterization, and adsorption behavior of aniline modified polystyrene resin for phenol in hexane and in aqueous solution Synthesis, characterization, and adsorption behavior of aniline modified polystyrene resin for phenol in hexane and in aqueous solution](/preview/png/611743.png)
Macroporous crosslinked poly(p-vinylbenzylaniline) (PVBA) was synthesized and its adsorption isotherms for phenol in hexane and in aqueous solution were comparatively measured. It was shown that the adsorption isotherms in hexane were straight lines and passed through the origin, whereas those in aqueous solution could be simulated by Freundlich isotherms. Adsorption enthalpies of phenol onto PVBA were calculated, and the results indicated that the adsorption was an exothermic process. Comparison of the adsorption behaviors of PVBA, poly(p-vinylbenzylmethylamine) (PVBMA), and poly(p-vinylbenzyl-p -nitroaniline) (PVBNA) for phenol in hexane suggested that hydrogen bonding and π–ππ–π stacking were primarily responsible for the adsorption, the nitrogen atom and benzene ring of PVBA acted as hydrogen bonding acceptors and formed hydrogen bonding with the hydrogen atom of hydroxyl group of phenol. Investigation of the adsorption mechanism in aqueous solution revealed that hydrogen bonding and hydrophobic interaction were the main driving forces.
Adsorption isotherms of phenol onto PVBA in hexane and aqueous solution with the temperature at 293, 298, 303, and 308 K, respectively.Figure optionsDownload as PowerPoint slide
Journal: Journal of Colloid and Interface Science - Volume 317, Issue 2, 15 January 2008, Pages 434–441