Hydration of γ-Al2O3 is often reported to occur via the superficial transformation of the alumina surface into aluminum hydroxide-like layers. However, very little evidence has been given so far to support this hypothesis. It is demonstrated here by X-ray diffraction, TEM, electron diffraction, and solubility studies that a second process of hydration takes place that involves the dissolution of alumina and subsequent precipitation of well-shaped Al(OH)3 particles from supersaturated alumina aqueous solution. This process can be observed on a macroscopic scale (XRD, TEM) for any pH⩾5pH⩾5, provided that the contact time between alumina and water exceeds 10 h. The least thermodynamically stable phase of aluminum hydroxide, bayerite, becomes favored compared with gibbsite when the pH of the solution is increased. It is assumed that the rate of formation of bayerite germs is greater than that of gibbsite due to variations in aluminum speciation in solution as a function of pH.
It is demonstrated here that the hydration of γ-Al2O3 involves the dissolution of alumina and the subsequent precipitation of well-shaped Al(OH)3 particles from supersaturated alumina aqueous solution.Figure optionsDownload as PowerPoint slide
Journal: Journal of Colloid and Interface Science - Volume 308, Issue 2, 15 April 2007, Pages 429–437