The adsorption and reaction of a titanate coupling reagent on the surfaces of different nanoparticles in supercritical CO2

The adsorption and reaction in supercritical CO2 of the titanate coupling reagent NDZ-201 on the surfaces of seven metal oxide particles, SiO2, Al2O3, ZrO2, TiO2 (anatase), TiO2 (rutile), Fe2O3, and Fe3O4, was investigated. FTIR and TG analysis indicated that the adsorption and reaction were different on different particle surfaces. On SiO2 and Al2O3 particles, there was a chemical reaction of the titanate coupling reagent on the surfaces. On the surfaces of ZrO2 and TiO2 (anatase) particles, there were two kinds of adsorption, weak and strong adsorption. On the surfaces of TiO2 (rutile), Fe2O3, and Fe3O4 particles, there was only weak adsorption. The acidity or basicity of the OH groups on the particle surface was the key factor that determined if a surface reaction occurred. When the OH groups were acidic, the titanate coupling reagent reacted with these, but otherwise, there was no reaction. The surface density of OH groups on the original particles and the amount of titanate coupling reagent adsorbed and reacted were estimated from TG analysis. The reactivity of the surface OH groups of Al2O3 particles was higher than that of the SiO2 particles.

The reaction and adsorption of the titanate coupling reagent depend on the acid–base property of the OH groups on the particle surface.Figure optionsDownload as PowerPoint slide