Characterization of early-age hydration processes in lime-ceramic binders using isothermal calorimetry, X-ray diffraction and scanning electron microscopy
ترجمه فارسی عنوان
تشخیص پروسه های هیدراتاسیون زودرس در باند آهک-سرامیک با استفاده از کولوریمتری ایزوترمال، پراش اشعه ایکس و میکروسکوپ الکترونی اسکن
کلمات کلیدی
آهک سرامیکی، هیدراتاسیون در سنین اولیه، کالریمتری ایزوترمال، پراش اشعه ایکس، میکروسکوپ الکترونی اسکن، ویژگی های مکانیکی،
موضوعات مرتبط
مهندسی و علوم پایه مهندسی شیمی جریان سیال و فرایندهای انتقال
چکیده انگلیسی
Early-age hydration processes in a lime-ceramic-water system are analyzed within the whole range of possible lime/ceramic ratios. The isothermal calorimetry shows a substantial effect of the heat of wetting on the total heat evolved, ranging from 10 J/g for lime to 3.9 J/g for ceramic. The highest specific hydration heat of 63 J/g during the analyzed 300-h hydration period exhibits the blended binder containing 70% ceramic and 30% lime which correlates well with the highest compressive and bending strengths of the paste prepared using this blend. Portlandite, ettringite and calcite are the main phases identified by the X-ray diffraction analysis after the hydration of ceramic-rich blends. According to the results of scanning electron microscopy, the initial course of pozzolanic reaction is for this type of binders characterized by the transition from tobermorite-like calcium-silicate-hydrate structures into jennite-like structures within the first 48 h. Blends with the ceramic content lower than 70% show a high portion of portlandite, calcite is present in low amount, and the jennite-like structures are observed after 48 h, following the initial formation of components with a very high Ca content. The favorable properties of the ceramic-rich blended binders can be explained by the partial hydraulic character of the ceramic. With the specific hydration heat of 29 J/g after 300 h and compressive strength of the paste 2.8 MPa after 30 days, the applied waste ceramic dust from the hollow brick production has good prerequisites for the application in lime-based binders with satisfactory engineering properties and good economical parameters for the building practice.