کد مقاله | کد نشریه | سال انتشار | مقاله انگلیسی | نسخه تمام متن |
---|---|---|---|---|
7004733 | 1454998 | 2013 | 11 صفحه PDF | دانلود رایگان |
عنوان انگلیسی مقاله ISI
Assessing the influence of shear stress and particle impingement on inhibitor efficiency through the application of in-situ electrochemistry in a CO2-saturated environment
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی شیمی
شیمی کلوئیدی و سطحی
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Assessing the influence of shear stress and particle impingement on inhibitor efficiency through the application of in-situ electrochemistry in a CO2-saturated environment Assessing the influence of shear stress and particle impingement on inhibitor efficiency through the application of in-situ electrochemistry in a CO2-saturated environment](/preview/png/7004733.png)
چکیده انگلیسی
An investigation was conducted to assess the performance of a commercially available high shear carbon dioxide (CO2) corrosion inhibitor in a series of flow-induced corrosion and erosion-corrosion environments. The purpose of the study was to understand the role that high shear stress and sand particle impingement play in influencing the in-situ corrosion rate of API 5L X65 carbon steel in blank and inhibited conditions. Tests were conducted at 45 °C in CO2-saturated conditions using a rotating cylinder electrode (RCE) for low shear stress tests (18-260 Pa) and a submerged impinging jet (SIJ) for high shear environments (104-740 Pa). The inhibitor was studied at concentrations of 0, 25, 50, 75 and 100 ppm. The application of computational fluid dynamics to model the SIJ and the use of ring shaped samples allowed for an accurate prediction of shear stress across the specimen surface that could be correlated with in-situ corrosion rate and inhibitor efficiency over a range of concentrations. The incorporation of 500 mg/L of sand to the system helped to quantify the increase of the in-situ corrosion rate due to the impingement of the particles. All corrosion rates were determined through the application of linear polarization measurements throughout the duration of the test. Post-test analysis of the material degradation mechanisms was examined using scanning electron microscopy (SEM).
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Wear - Volume 304, Issues 1â2, 15 July 2013, Pages 49-59
Journal: Wear - Volume 304, Issues 1â2, 15 July 2013, Pages 49-59
نویسندگان
O.O. Ige, R. Barker, X. Hu, L.E. Umoru, A. Neville,