عنوان انگلیسی مقاله ISI
Thermal Shock Failure Mechanism of Nanostructured Zirconia Coating by Atmospheric Plasma Spraying
ترجمه فارسی عنوان
مکانیسم شکست ناپذیر شوک حرارتی پوشش نیکل زیرکونیا توسط پاشش پلاسمای جو
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
شکست شوک حرارتی، پوشش زیرکونیا، پاشش پلاسما اتمسفر،
موضوعات مرتبط
مهندسی و علوم پایه
سایر رشته های مهندسی
مکانیک مواد
چکیده انگلیسی
Nanostructured zirconia coatings has been prepared based on reasonable spraying technical parameters and the corresponding thermal shock property of the as-sprayed coating was examined at 1100 °C. The structure and the surface/interface morphology of the coatings have been analyzed using X-ray diffraction (XRD), metallographic microscope, scanning electron microscopy (SEM), energy dispersive spectrum (EDS) and transmission electron microscopy (TEM). Based on the detailed analysis of the structure and phase composition, a rational mechanism has been proposed for thermal shock failure of the coating. Compared with other nanoparticles, those particles close to pores and pre-existing microcracks would preferentially grow up during the thermal shock process due to a better growth space. The growth of these nanoparticles is conducive to the formation of new microcracks which would lead to the growth of the other nanoparticles. With the growth of most or all of the nanoparticles, the nanostructured zirconia coating correspondingly changes into the quasi-microstructured coating. The thermal shock failure mode of the as-sprayed coating is similar to that of traditional zirconia thermal barrier coatings (TBCs).
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Rare Metal Materials and Engineering - Volume 46, Issue 3, March 2017, Pages 601-605
Journal: Rare Metal Materials and Engineering - Volume 46, Issue 3, March 2017, Pages 601-605
نویسندگان
Chang Ying, Liu Bei, Dong Shijie, Wang Huihu, Xie Zhixiong,