Microstructure and material properties of porous hydroxyapatite-zirconia nanocomposites using polymethyl methacrylate powders
ترجمه فارسی عنوان
ریزساختار و خواص مواد نانوکامپوزیت های هیدروکسی آپاتیت متشکل از زیرکونیا متخلخل با استفاده از پودرهای پلی متیل متاکریلات
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
نانوکامپوزیت ها، ساختار متخلخل خواص مواد،
موضوعات مرتبط
مهندسی و علوم پایه
سایر رشته های مهندسی
مهندسی (عمومی)
چکیده انگلیسی
Bone like porous monolithic hydroxyapatite (HAp) and hydroxyapatite-zirconia (HAp-ZrO2) nanocomposites were fabricated by a pressureless sintering process with polymethyl methacrylate (PMMA) powders as the pore forming agent. It was found that such powders could be successfully removed by a burning-out process, leaving the sintered body with randomly distributed pores. The material properties, i.e., the pore morphology, compressive strength and elastic modulus, could be changed dramatically by increasing the pore forming agent. With 50Â vol.% of the agent, both the porous monolithic HAp and HAp-ZrO2 nanocomposites formed interconnected porous microstructures. The compressive strengths of porous monolithic HAp and HAp-ZrO2 nanocomposites were about 31.4 and 34.9Â MPa, respectively. Their elastic moduli were about 19.6Â GPa and 23.4Â GPa, respectively, which are almost the same as those of the human cortical bones. Porous HAp-ZrO2 nanocomposites exhibited better compressive strengths and elastic moduli than that of porous monolithic HAp bodies due to the strengthening effect of high strength and toughened reinforcing bio-inert ZrO2 nano-particles.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials & Design - Volume 67, 15 February 2015, Pages 136-144
Journal: Materials & Design - Volume 67, 15 February 2015, Pages 136-144
نویسندگان
Asit Kumar Gain, Liangchi Zhang, Weidong Liu,