Lifetime prediction of low infrared emissivity coatings in 3 wt% NaCl solution
موضوعات مرتبط
مهندسی و علوم پایه سایر رشته های مهندسی کنترل و سیستم های مهندسی
پیش نمایش صفحه اول مقاله
Lifetime prediction of low infrared emissivity coatings in 3 wt% NaCl solution
چکیده انگلیسی

Low infrared emissivity coatings were prepared by using epoxy–polyurethane (EPU) and aluminum (Al) as adhesives and fillers, respectively. The change of coating emissivity was studied by using immersion testing in 3 wt% NaCl solution to assess the corrosion resistance. It was found that the emissivity increased with increasing heating temperature and time, and that the emissivity of coating failure increased with decreasing Mach number. Moreover, the Arrhenius relationship was employed to calculate the lifetime of low infrared emissivity EPU/Al composite coatings. The calculated results when compared with observation data validate the effectiveness of the model predictions. The current work showed that the low emissivity EPU/Al composite coatings exhibited favorable lifetime, and the Arrhenius relationship was effective and showed a potential in engineering applications.


► The emissivity of the coating increased with increasing heating temperature and time.
► The emissivity of coating failure increased with decreasing Mach number.
► The lifetime of the coatings was predicted on the basis of Arrhenius relationship.
► Arrhenius relationship was effective for the lifetime of low emissivity coatings.