Structure and photoluminescence properties of ZnS films grown on porous Si substrates

ZnS films were deposited on porous silicon (PS) substrates with different porosities. With the increase of PS substrate porosity, the XRD diffraction peak intensity decreases and the surface morphology of the ZnS films becomes rougher. Voids appear in the films, due to the increased roughness of PS structure. The photoluminescence (PL) spectra of the samples before and after deposition of ZnS were measured to study the effect of substrate porosity on the luminescence properties of ZnS/PS composites. As-prepared PS substrates emit strong red light. The red PL peak of PS after deposition of ZnS shows an obvious blueshift. As PS substrate porosity increases, the trend of blueshift increases. A green emission at about 550 nm was also observed when the porosity of PS increased, which is ascribed to the defect-center luminescence of ZnS. The effect of annealing time on the structural and luminescence properties of ZnS/PS composites were also studied. With the increase of annealing time, the XRD diffraction peak intensity and the self-activated luminescence intensity of ZnS increase, and, the surface morphology of the ZnS films becomes smooth and compact. However, the red emission intensity of PS decreases, which was associated with a redshift. White light emission was obtained by combining the luminescence of ZnS with the luminescence of PS.

► We study the possibility of using ZnS and PS for fabrication of optoelectronic devices.
► Structure and photoluminescence properties of ZnS/PS composites are studied in detail.
► After deposition of ZnS, the red PL peak of PS shows an obvious blueshift.
► Substrate porosity and annealing time can affect luminescence properties of ZnS/PS composites.
► Combining blue, green emission of ZnS with red emission of PS, white light emission is obtained.