Room-temperature growth of thin films of niobium on strontium titanate (0 0 1) single-crystal substrates for superconducting joints

With the eventual aim of forming joints between superconducting wires of YBa2Cu3O7−δ (YBCO), thin films of Nb were grown at room-temperature on SrTiO3 (STO) (0 0 1), a single-crystal substrate that shows good lattice matching with YBCO. The crystallinity, surface morphology, and superconducting properties of the Nb thin films were investigated and compared with those of similar films grown on a silica glass substrate. The Nb thin films grew with an (hh0) orientation on both substrates. The crystallinity of the Nb thin films on the STO substrate was higher than that on the silica glass substrate. X-ray diffraction measurements and observation of the surface morphology by atomic-force microscopy indicated that Nb grew in the plane along the [1 0 0] and [0 1 0] directions of the STO substrate. This growth mode relaxes strain between Nb and STO, and is believed to lead to the high crystallinity observed. As a result, the Nb thin films on the STO substrates showed lower electric resistivity and a higher superconducting transition temperature than did those on the silica glass substrates. The results of this study should be useful in relation to the production of superconducting joints.