Electrophoretic deposition of aramid nanofibers on carbon fibers for highly enhanced interfacial adhesion at low content

Here, an anodic electrophoretic deposition was adopted to facilitate the large-scale uniform coating of nano-fillers onto carbon fibers to enhance the interfacial properties between carbon fibers and epoxy matrix. As interface-reinforcing materials, aramid nanofibers were introduced because of their superior mechanical properties and epoxy matrix-friendly functional groups. Furthermore, aramid nanofibers can be readily coated on carbon fibers via electrophoretic deposition because they are negatively-charged in solution with high electrical mobility. Finally, aramid nanofiber-coated carbon fibers showed significantly improved interfacial properties such as higher surface free energy and interfacial shear strengths (39.7% and 34.9% increases, respectively) than those of a pristine carbon fiber despite a very small amount of embedding (0.025 wt% of aramid nanofibers in a carbon fiber), and the short beam strength of the laminated composite prepared with the aramid nanofiber-coated carbon fibers was also improved by 17.0% compared to a non-modified composite.