Three-dimensional assessment of low velocity impact damage in particle toughened composite laminates using micro-focus X-ray computed tomography and synchrotron radiation laminography

Results are presented studying the contribution of particle toughening to impact damage resistance in carbon fibre reinforced polymer materials. Micro-focus X-ray computed tomography and synchrotron radiation computed laminography were used to provide a novel, multiscale approach for assessing impact damage. Thin (1 mm thick) composite plates containing either untoughened or particle-toughened resin systems were subjected to low velocity impact. Damage was assessed three-dimensionally at voxel resolutions of 0.7 μm and 4.3 μm using SRCL and μCT respectively; the former being an innovative approach to the laterally extended geometry of CFRP plates. Observations and measurements taken from μCT scans captured the full extent of impact damage on both material systems revealing an interconnected network of intra- and inter-laminar cracks. These lower resolution images reveal that the particle-toughened system suppresses delaminations with little effect on intralaminar damage. The higher resolution images reveal that the particles contribute to toughening by crack deflection and bridging.